By mechanical embossing equipment in a stainless steel plate, the plate surface appears uneven pattern.

Beginning in the early 1960s by a small batch of large rolling mills in Europe, then as stainless steel checkered excellent corrosion resistance and slip resistance have been adopted in many industries and thus began to spread.

First stainless steel checkered pattern style for horizontal and vertical stripes interleaved, domestic Shanxi Taiyuan and Shanghai Baosteel Group in production in the next 20 - 30 years after researchers continue to experiment with better and improve the skid resistance pattern design out large-scale production is now promoted and applied. In recent years, the use of stainless steel checkered plate are constant innovation, breakthrough, change, applicable industry and product models are constantly increasing, product replacement rate and more frequent.

Applications

The decorative plate has the advantages of beautiful appearance, anti slip, strong performance, steel saving, etc..

It is widely used in the fields of transportation, architecture, decoration, equipment, floor, machinery, shipbuilding and so on.

In general, use is not high requirements of mechanical properties, the mechanical properties of tread plate, so tread plate quality mainly flowering rate, pattern height pattern, pattern height.

The difference between Checkered and etching

Checkered plates create decorative effects of textures and patterns by embossing or printing on the surface of stainless steel.

This processing method can enable stainless steel materials to exhibit various unique textures and patterns, such as lines, squares, waves, etc.

The stainless steel patterned plate has a distinct appearance effect, giving people a sense of aesthetics and decoration.

It can be used in fields such as architectural decoration, interior decoration, and furniture production, providing a variety of decoration options for walls, ceilings, stair railings, furniture surfaces, etc.

The design of stainless steel patterned panels can be coordinated with architectural style and interior design, creating personalized and unique spatial effects.

Etching plate is another common surface treatment method for stainless steel.

Etching plates are formed by coating a chemical solution or acidic solution on the surface of stainless steel and forming patterns and textures through chemical reactions.

Compared with stainless steel checkered patterned plates, etched plates can achieve more refined and complex designs.

Through the etching process, detailed and precise patterns, such as text, images, etc., can be formed on the surface of stainless steel.

Details of commonly available used checkered/embossed

Pattern	Grade	Thickness (mm)	Width (mm)	Origin
Bean type	304 304L 321 316L309S 310S etc	0.4mm-14.0mm	≤1500mm	TISCO / ZPSS / JISCO etc
“T”type	304 304L 321 316L 309S 310S etc	1.0mm-5.0mm	≤1500mm	TISCO / ZPSS / JISCO etc
European pattern type	304 304L 321 316L 309S 310S etc	0.8mm-8.0mm	≤1500mm	TISCO / ZPSS / JISCO etc
Japanese pattern type	304 304L 321 316L 309S 310S etc	0.4mm-14.0mm	≤1500mm	TISCO / ZPSS / JISCO etc
Round pattern type	304 304L 321 316L 309S 310S etc	0.3mm-3.0mm	≤1500mm	TISCO / ZPSS / JISCO etc
4 lines pattern type	304 304L 321 316L 309S 310S etc	0.3mm-3.00	≤1500mm	TISCO / ZPSS / JISCO etc
linen Pattern	304 304L 321 316L 309S 310S etc	0.4mm-2.0mm	≤1219mm	TISCO / ZPSS / JISCO etc
Stone pattern	304 304L 321 316L 309S 310S etc	0.4mm-3.0mm	≤1219mm	TISCO / ZPSS / JISCO etc
Etching pattern	304 304L 321 316L 309S 310S etc	0.4mm-3.0mm	≤1219mm	TISCO / ZPSS / JISCO etc
Perforated pattern	304 304L 321 316L 309S 310S etc	0.4mm-3.0mm	≤1219mm	TISCO / ZPSS / JISCO etc

Chemical composition and Mechanical properties

牌号 Grade		C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)	Ni(%)	N(%)	Mo(%)
奥氏体 Austenitic	201	≤0.15	≤1.00	5.50-7.50	≤0.06	≤0.03	16.00-18.00	0.50-1.00	≤0.25	-
	202	≤0.15	≤1.00	7.50-10.00	≤0.06	≤0.03	17.00-19.00	2.00-4.00	≤0.25	-
	304	≤0.08	≤1.00	≤2.00	≤0.045	≤0.03	18.00-20.00	8.00-10.50	≤1.00	-
	304L	≤0.03	≤1.00	≤2.00	≤0.045	≤0.03	18.00-20.00	8.00-12.00	≤1.00	-
	321	≤0.08	≤1.00	≤2.00	≤0.045	≤0.03	17.00-19.00	9.00-12.00	≤1.00	-
	316L	≤0.03	≤1.00	≤2.00	≤0.045	≤0.03	16.00-18.00	10.00-14.00	≤1.00	2.00-3.00
	309S	≤0.08	≤1.00	≤2.00	≤0.045	≤0.03	22.00-24.00	12.00-15.00	-	-
	310S	≤0.08	≤1.50	≤2.00	≤0.045	≤0.03	24.00-26.00	19.00-22.00	-	-

铁素体 Ferritic	430	≤0.12	≤1.00	≤1.00	≤0.04	≤0.03	16.00-18.00	0.50-0.75	-	-

牌号 Grade		TS (Mpa)	YS (Mpa)	EL ( %)	Rate of reduction in area (%)	Density (g/cm³）	Hardness (HB / HRB / HV)
奥氏体 Austenitic	201	≥520	≥275	50-60	≥60	7.93	≤187HB / ≤90HRB / ≤200HV
	202	≥520	≥275	50-60	≥45	7.93	≤207HBS / ≤95HRB / ≤218HV
	304	515-1035	≥205	≥40	≥60	7.93	≤201HBW / ≤92HRB / ≤210HV
	304L	≥520	≥205	≥40	≥60	7.93	≤187HB / ≤90HRB / ≤200HV
	321	≥520	≥205	≥50	≥40	7.98	≤187HB / ≤90HRB / ≤200HV
	316L	≥480	≥177	≥40	≥60	7.98	≤187HB / ≤90HRB / ≤200HV
	309S	≥515	≥205	≥40	≥50	7.98	≤187HB
	310S	≥515	≥205	≥40	≥50	7.98	≤187HB

铁素体 Ferritic	430	≥450	≥205	≥22	-	7.75	≤183HBW / ≤89HRB / ≤200HV

Commonly used checkered pattern