316L grade has a lower carbon content , which is commonly used in pulp and paper equipment heat exchangers, dyeing equipment, film washing equipment, pipelines, coastal areas outside the building materials. Corrosion resistance is better than 316 material.
Production Standards
|
Grade
|
GB/T 1220-2007
|
ASTM
|
DIN
|
JIS
|
KS
|
|
316L
|
022Cr17Ni12Mo
|
316L
|
1.4404
|
SUS316L
|
STS316L
|
Chemical Composition
|
Grade
|
C(%)
|
Si(%)
|
Mn(%)
|
P(%)
|
S(%)
|
Cr(%)
|
Ni(%)
|
Mo(%)
|
Cu(%)
|
|
316L
|
≤0.03
|
≤1.0
|
≤2.0
|
≤0.045
|
≤0.03
|
16.0-18.0
|
10.0-14.0
|
2.0-3.0
|
----
|
Mechanical Properties
|
Grade
|
TS
Mpa
|
YS
Mpa
|
EL
(%)
|
Rate of reduction in area
(%)
|
Density
(g/cm3)
|
|
316L
|
≥480
|
≥177
|
≥40
|
≥60
|
7.98
|
Specifications
|
Available technical
|
Available thickness
(mm)
|
Available width
(mm)
|
Available finish
|
Available origin
|
|
Cold rolled
|
0.4-6.0
|
Standard:1000 1219 1500
Special:can be ordered
|
2B / No.4 / HL / BA / Mirror/Checkered/Colored etc
|
TISCO / ZPSS . JISCO etc
|
|
Hot rolled
|
3.0-80
|
Standard:1500 1800 2000
Special:can be ordered
|
No.1/No.4/HL/Mirror etc
|
TISCO / ZPSS / JISCO etc
|
Applications
- Widely used in pulp and paper equipment heat exchangers, dyeing equipment, film washing equipment, pipelines, coastal areas outside the building materials, marine, industrial air field.
- Used in the field of solenoid valve, mainly used in the shell, clamp, ball, valve body, valve seat, nut, stem and so on.
- Used in marine environment, standard welding method for welding.