410S belongs to martensitic stainless steel. 410S is one of the lowest content of Cr in ferritic stainless steel, it has the property of stainless steel, and the corrosion resistance is better than that of 410 420 420J1 420J2 martensitic stainless steel with high carbon content.
It has good plasticity, toughness and cold formability, and is superior to other ferritic stainless steel with higher Cr content. When the C content of 410S stainless steel is very low, the plasticity and toughness of the stainless steel can be significantly improved.
So 410S stainless steel is mainly used in the manufacture of water vapor, ammonium bicarbonate solution, parts and equipment of the oil sulfur corrosion heat lining etc..
Chemical Composition
|
Grade
|
C(%)
|
Si(%)
|
Mn(%)
|
P(%)
|
S(%)
|
Cr(%)
|
Ni(%)
|
|
410
|
≤0.15
|
≤1.0
|
≤1.0
|
≤0.035
|
≤0.03
|
11.5-13.5
|
≤0.6
|
|
410S
|
≤0.08
|
≤1.0
|
≤1.0
|
≤0.035
|
≤0.03
|
11.5-13.5
|
≤0.6
|
Mechanical Properties
|
Grade
|
TS
Mpa
|
YS
Mpa
|
EL
(%)
|
Rate of reduction in area
(%)
|
Density
(g/cm3)
|
|
410
|
≥490
|
≥345
|
≥24
|
≥60
|
7.75
|
|
410S
|
≥490
|
≥345
|
≥24
|
≥60
|
7.75
|
Specifications
|
Available technical
|
Available thickness
（mm）
|
Available width
（mm）
|
Available finish
|
Available origin
|
|
Hot rolled
|
3.0 - 100
|
Standard :1000 1219
Special width:can be ordered
|
No.1
|
TISCO etc
|
Applications
410/410S is to improve the corrosion resistance of the steel and formability of steel, mainly used in the manufacture of water vapor, ammonium bicarbonate solution, parts and equipment of the oil sulfur corrosion heat lining etc..
Different Production Standards
|
Grade
|
GB
|
ASTM
|
DIN
|
JIS
|
|
410
|
1Cr13
|
410
|
1.4006
|
SUS410
|
|
410S
|
0Cr13
|
410S
|
1.4000
|
SUS410S
|